ABS-like 3D resin, White, 1L

Tuotenro
ABS-like_3D_resin_White_1L
Varastossa
43,93 EUR 35,00 EUR
3D printing resin, white, 1L, 405nm UV Cure

90% ABS 3D resin

Anti-scratch

Super strong and tenacity

Great weathering

Suitable for different post processing like drilling, screwing etc.

Non VOC, RoHS certificated

Technical specification
Flexural modulus 1.192-2.525Mpa
Flexural strenght 68-80MPa
Hot deformation temp 65C
Linear shrinkage 1.05-1.35%
Tensile strenght 42-62MPa
Tensile modulus 1.86-2.645MPa
Elongation at break 4-10%
Hardness (Shore D) 82-85D
Viscosity 150-350MPa-s
Printing parameter

ABS-like resins are perfectly on most brand LCD printer, and fast printing on DLPs.


Printing time For LCD printer, bottom layer 30-70s and each  layer  exposure time  4-12s, for example, layer thickness 50 micron on Anycubic printer, base 50s while each layer 8s.
For DLP printer, bottom 5-15s and each layer 1-5s.
Cleaning and post-curing 1), Spray with Isopropanol, then blow resin away with cool wind.
2) Prepare two containers with Isopropanol (alcohol> 95%), and place the jobs into the first container and slightly shake it, then soak in the second container for about 1 minute
3)Flush with water before dry it, do make it sure it ‘s 100% dried as residuary alcohol may cause white spot or crack on jobs.
Post-curing 1) The curing time is proportional to the volume of the work piece and inversely proportional to the optical power of the curing chamber. Example: 100 watt LED curing box, jewelry jobs is recommended to be cured with soaking in water for 20-30 minutes.
2) The post-cure time of dental casting resin, dental non-casting resin and jewelry mold resin shall not more than 5 minutes.
3) Work-pieces should be in the water during post-curing to prevent deformation especially for dental and jewelry.
4) Don’t forget to use cool air to dry it after post-curing.